Jinming glaze, as well as one brick, select Jinming exported to South Korea glaze, life on the road is bright. Full cast Glaze Tidbits: Technology introduces touch, bright surface soft, smooth not projecting, it is shining brilliantly, glaze marbled texture clear, natural, and after integration of the upper transparent glaze, like a transparent crystal glaze film covering, making the overall level more clear perspective. Unlike ordinary glazed tiles, the glaze surface is wear special crystal glaze, high temperature sintering molecule completely closed, almost no gap, long time durability remains highlighted not bleak, hard wear. Mohs hardness of 6 degrees, the water absorption less than 0.5%, even texture than natural stone, compact, stable and secure. Hard edge with a coin scratch the tile surface, the surface no scratches or dregs phenomenon glazes, wear very advantageous. The glaze color glazed, its process is similar to the general body of glazed tiles, the main difference is that it finished in the end of the glaze is applied after printing, Zaishi surface layer of transparent glaze, the glaze after firing the entire surface of the blows part, to retain a part of the surface glaze layer, printing layer, bottom enamel glaze exported to Taiwan, the main objective is to replace the whole cast brick tiles. The main advantage of body without quality raw materials, as long as the surface of the glaze layer 0.5-1mm about it. The tiles have many fabric 2-3mm fine materials; polishing glazed tiles pattern simulation is very easy to do, the cost is low. Since the glaze firing speed, lower power consumption, power consumption is lower than the glaze polishing and polishing yields higher. The main disadvantage of the past cast glazed tiles technology equipment is not very mature, still less in the domestic mass-produced. This product has emerged in the international community for many years, particularly in Spain and Italy, but not a large number of applications, mainly due to technical obstacles and comparative advantage is not much before. Particularly in China, producing polished good material is also good, energy cost is not too high. But this situation has changed. Technical difficulties thick glaze firing is likely to occur when a large number of bubbles, so that the products after polishing antifouling ability, loss of light. The glaze is too book, then glazed total deformation, easy to produce leakage phenomenon throw or partially open at the end polishing. Therefore, mass production, product quality is difficult to guarantee superior product difficult to stabilize. To solve this problem, glazed and polished glaze process equipment should be a breakthrough. That is, to the surface of the glaze is not easy to produce bubbles when the firing, firing wide temperature range, expansion coefficient close to the body, so it is not easy when firing or throwing after deformation. Building and sanitary ceramics commonly used in emulsion glaze, due to the lack of transparent glaze covering power, it is difficult to cover up dirty brick, and environmental protection requirements and maximize the use of low-quality raw material, blank, transparent glaze therefore become more narrow range. Ceramic enterprises used the glaze opacifiers experienced tin oxide, zinc oxide, titanium dioxide, phosphates, until the process of zirconium silicate. However, tin oxide as emulsifying agent, due to high cost, use less and less. 1920s, began as a reference zircon glaze opacifiers, and later began using zircon substituted tin oxide, reducing the cost of tile glaze decoration products. But as in the conventional glaze added 5% tin oxide, can produce bluish-white glaze tone; zinc oxide is widely used within zircon glaze, can improve the degree of whiteness and Opaque. Sanitary ware products in high temperature zinc oxide glaze with a strong solvent action, can significantly reduce the viscosity of the glaze, so there are still some use, and they will not be completely ruled out; when the titanium oxide added to the glaze can be made of high-grade white opaque glaze exported to Japan glazes, it has proven to be a viable way formula. The role of phosphorus compounds in the glaze: one, used to make the glaze opaque emulsions; second, to increase the refractive index of the glaze of light, increase luster glaze. Calcium phosphate, ashes, apatite can be appropriate, with the right amount into the glaze so the glaze to form a good emulsion and light effects. Further lithium limestone, diopside and other lithium compounds are also good opaque glaze raw materials. Ningxia glazes, glazes, Zibo Boshan colored glaze factory Jinming (view) provided by Zibo Boshan Jinming color glaze factory. Zibo Boshan Jinming color glaze factory (www.jinmingglaze.com) is a professional, "transparent frit, zirconium white frit, titanium white frit, pigment" company. Since its inception, we adhere to the "good faith, sound management" approach, the courage to participate in healthy competition in the market, so that the "Zibo Boshan colored glaze factory Jinming" brand has a good reputation. We adhere to the "service first, customer first" principle, so Zibo Boshan Jinming color glaze factory has won the trust of customers congregation in ceramics, and establish a good corporate image. Special Note: This information is for reference only pictures and information, please contact us to obtain the most accurate information, thank you!